CPE CF112 Carbon
Description
Carbon-fibers-reinforced CPE HG100 filament was developed for its pressure resistance, hardness, and surface effect. The contained fibers ensure functionality, great printability, dimensional stability, and layer adhesion. The printed objects have a nice smooth surface.
This material is optimal for applications with long-term loads. It has higher wear resistance, heat distortion temperature, hardness, and chemical resistance in comparison with CPE HG100.
Features:
- High-technical durable long-life material
- Good interlayer adhesion
- Creep resistance (resistance against deformation under long-term load)
- Matte finish
- Wear resistance
- Temperature resistance up to 100 °C
- High hardness
- Chemical resistance against acids, alkalis, alcohols
- Easy printing
- Low warping
- Recyclable
- 25% Bio-based
- BPA-free & styrene-free
- Safe to use in electrical and electronic equipment
| Working temperature: | 255–275 °C |
| Heated bed: | 70–85 °C |
| Diameter: | 1.75 mm and 2.85 mm |
| Diameter tolerance: | +/- 0.10 mm |
| Weight: |
600 g of filament (+ 230 g spool)
|
| The length of the filament: |
200 m (1.75 mm, 600 g)
80 m (2.85 mm, 600 g)
|
| RAL | Pantone | HEX: |
N/A | N/A | N/A
|
- Abrasive – wear-resistant nozzles are recommended!
- 3D Printing Guide
- For a good adhesion use PVA glue or 3DLac. Due to a great adhesion to other materials, it can damage your bed without a separation layer of adhesive
- Moisture sensitive – keep in a protective resealable sachet
- Drying filaments before processing
- Spools Dimension
- Data Sheets
Comparison of our copolyester filaments:
| CPE CF112 Carbon | CPE HG100 | PETG | PETG filaments* | |
| Impact resistance | 106 kJ/m2 (unnotched) |
no break (notched) |
85 J/m (notched) |
98–126 J/m (notched) |
| Tensile strength | 52 MPa | 48 MPa | 50 MPa | 26–45 MPa |
| Elongation at break | 8 % | 150 % | 120 % | 58–110 % |
| Hardness | 94 R-Scale | 115 R-Scale | 105 R-Scale | 108 R-Scale |
| Flexural strength | / | 71 MPa | 71 MPa | 54–74 MPa |
| Flexural modulus | / | 1860 MPa | 2150 MPa | 1600–2100 MPa |
| Wear resistance | ★★★★ | ★★ | ★ | ★ |
| Creep resistance | ★★★★ | ★★ | ★ | ★ |
|
Heat resistance (HDT) |
up to 100 °C | 80 °C | 70 °C | 70 °C |
|
Chemical resistance to acids, bases, hydrocarbons |
good | good | poor | poor |
*publicly accessible information from other producers
The input material was carefully selected to achieve the best processability and final properties. Fillamentum’s products are always produced from the precisely specified type of material, with the highest stability across all the batches. The customers can rely on the best quality at any time they use our filament.